HDPE Virgin Granules/Shanghai Petrochemical Sh400u/Paint Buckets/Containers/Baffles/Waste Bins for Outdoor Use

• Material: High Density Polyethylene/HDPE
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: HDPE
• Plastic Forming Method: Film Pressure
• Color: White
• Transport Package: 25kg/Bag or as Customer′s Request.
• Specification: Granular
• Trademark: KUNLUN
• Origin: China
• Production Capacity: 5000 Tons/Month

Product Description

China factory priceHDPE/high density polyethylene granules / hdpe plastic raw material PE100


Product Description

HDPE has the advantages of excellent comprehensive properties, good chemical stability, good shape processing performance and relatively low cost.
HDPE can adapt to a wider range of application requirements through modifying, copolymerization, grafting,blending, reinforced filling, transparency, filling, weather resistance.

Specification

HDPE specification

HDPE cable material Property	Unit	Typical Value
Mass density	g/cm 3	0.941-0.959
Melt flow Rate(190 centidegree /2.16kg)	g/10min	≤1.0
Tensile yield strength	MPa	≥19.0
Flexural modulus	Mpa	≥965
Elongation@ break	%	≥400
Impact Embrittlement temperature	centidegree	MAX -118
Dielectric Constant	100KHZ	2.32
Dielectric Constant	1MHZ	2.31
Loss Tangent	100KHZ	MAX 0.0001
Loss Tangent	1MHZ	MIN 1x10 15

LDPE Specification

Physical Properties	Test Method	Nominal Value	Unit
Density	ISO 1183	0.921	g/cm3
Melt Mass-Flow Rate (MFR)	ISO 1133	1.9	g/10min
Hardness
Shore Hardness (shore D)	ISO 868	45
Mechanical Properties
Tensile Modulus	ISO 527-2	175	MPa
Tensile Strength  Yield,	ISO 527-2	9.0	MPa
Tensile Strength Break,	ISO 527-2	13.0	MPa
Tensile Strain(Break)	ISO 527-2	850	%
Modulus of Elasticity	Internal Method	250	MPa
Thermal
Vicat Softening Temperature	ISO 306/A50	89.0	°C
Melting Temperature (DSC)	DIN 53765	108	°C
Peak Crystallization Temperature (DSC)	DIN 53765	97.0	°C
Heat of Fusion	DIN 53765	110	J/g
Electrical
Volume Resistivity	ASTM D257	8.5E+15	ohm •cm
Dielectric Strength	ASTM D149	30.0	kV/mm
Dielectric Constant (60Hz)	ASTM D150	2.20	%
Dissipation Factor (60 Hz)	ASTM D150	0.00050

Application

HDPE used for packaging film, rope, woven bags, fishing nets, water pipe; Injection moulding lowgrade commodity and shell, the load bearing components of glue box, turnover box; 

1. HDPE Film grade is widely used in the production of packing bag, film etc.

2. Blow Molding grade is for making various bottles, cans, tanks , barrels.

3. Injection Molding grade is for making food cases, plastic trays, goods containers.

Package
25 Kgs PE Bag