Pipe Grade Virgin HDPE PE100 Black Color Granules HDPE PE 100 Resin HDPE Granules

• Customization: Available
• Material: High Density Polyethylene/HDPE
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Model NO.: HDPE LDPE LLDPE
• Plastic Forming Method: Film Pressure
• Color: White
• Transport Package: 25kg/Bag or as Customer′s Request.
• Specification: Granular
• Trademark: KUNLUN
• Origin: China
• Production Capacity: 5000 Tons/Month

Product Description

China factory priceHDPE/high density polyethylene granules / hdpe plastic raw material PE100


Product Description

HDPE has the advantages of excellent comprehensive properties, good chemical stability, good shape processing performance and relatively low cost.
HDPE can adapt to a wider range of application requirements through modifying, copolymerization, grafting,blending, reinforced filling, transparency, filling, weather resistance.

Specification

Product name	HDPE Granules
Type	Plastic Raw Materials Granules
Color	Transparent and other colors
Shape	Pellet - Granules
Application	Packaging of all kinds of articles
Density	0.924 g/cm3
MFR	0.6 - 0.8 G/10 Min
Melting point	110~115ºC
Processing	150~210ºC

Film Grade

Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C

Blow Grade

Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%

Injection Grade

Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR	---	ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

HDPE Cable Grade

Property	Unit	Typical Value
Mass density	g/cm3	0.941-0.959
Melt flow Rate(190 centidegree /2.16kg)	g/10min	≤1.0
Tensile yield strength	MPa	≥19.0
Flexural modulus	Mpa	≥965
Elongation@ break	%	≥400
Impact Embrittlement temperature	Centidegree	MAX -118
Dielectric Constant	100KHZ 1MHZ	2.32 2.31
Loss Tangent	100KHZ 1MHZ	MAX 0.0001 MAX 0.0001
Volume resistivity	OHM-CM	MIN 1x10 15
Application	Mainly used for the production of high toughness of the telephone,cable insulation material

 

Application

HDPE used for packaging film, rope, woven bags, fishing nets, water pipe; Injection moulding lowgrade commodity and shell, the load bearing components of glue box, turnover box; 

1. HDPE Film grade is widely used in the production of packing bag, film etc.

2. Blow Molding grade is for making various bottles, cans, tanks , barrels.

3. Injection Molding grade is for making food cases, plastic trays, goods containers.

Package
25 Kgs PE Bag