CAS No.: | 9002-88-4 |
---|---|
Formula: | (C2h4)N |
Material: | Polyethylene/PE |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product name
|
HDPE Granules
|
Type
|
Plastic Raw Materials Granules
|
Color
|
Transparent and other colors
|
Shape
|
Pellet - Granules
|
Application
|
Packaging of all kinds of articles
|
Density
|
0.924 g/cm3
|
MFR
|
0.6 - 0.8 G/10 Min
|
Melting point
|
110~115ºC
|
Processing
|
150~210ºC
|
Item
|
Test condition
|
Test Method
|
Value
|
Unit
|
Density
|
|
ISO 1183
|
0.944-0.955
|
g/cm3
|
MFR
|
190°C/2.16kg
|
ISO 1133
|
0.03-0.07
|
g/10min
|
Tensile strength at yield
|
|
ISO 527-2
|
22
|
MPa
|
Elongation at break
|
|
ISO 527-2
|
>350
|
%
|
ESCR
|
F50,50°C,100%
|
ASTM D-1693A
|
1000
|
h
|
VICAT
|
|
ASTM D-1525
|
126
|
°C
|
Item
|
Test Condition
|
Test Method
|
Value
|
Unit
|
Density
|
|
ISO 1183
|
0.950~0.955
|
g/cm3
|
MFR
|
190°C/2.16kg
|
ISO 1133
|
1.7~2.5
|
g/10min
|
Tensile strength at yield
|
|
ISO 527-2
|
24
|
MPa
|
Elongation at break
|
|
ISO 527-2
|
>600
|
%
|
Item
|
Test Condition
|
Test Method
|
Value
|
Unit
|
MFR
|
190°C/2.16kg
|
ASTM D-1238
|
20
|
g/10min
|
Density
|
---
|
ASTM D-792
|
0.954
|
g/cm3
|
Tensile strength at yiled
|
---
|
ASTM D-638
|
28
|
MPa
|
Elongation at break
|
---
|
ASTM D-638
|
250
|
%
|
Impact tensile strength
|
---
|
ASTM D-1822
|
42
|
kJ/m2
|
ESCR
|
---
|
ASTM D-1693
|
3
|
---
|
VACIT
|
---
|
ASTM D-1525
|
127
|
°C
|
Property
|
Unit
|
Typical Value
|
Mass density
|
g/cm3
|
0.941-0.959
|
Melt flow Rate(190 centidegree /2.16kg)
|
g/10min
|
≤1.0
|
Tensile yield strength
|
MPa
|
≥19.0
|
Flexural modulus
|
Mpa
|
≥965
|
Elongation@ break
|
%
|
≥400
|
Impact Embrittlement temperature
|
Centidegree
|
MAX -118
|
Dielectric Constant
|
100KHZ 1MHZ |
2.32 2.31 |
Loss Tangent
|
100KHZ 1MHZ |
MAX 0.0001 MAX 0.0001 |
Volume resistivity
|
OHM-CM
|
MIN 1x10 15
|
Application
|
Mainly used for the production of high toughness of the telephone,cable insulation material
|